Nano-Adamant unmodified nano silica layers for HPTLC
Glass plates
nano silica 60, specific surface (BET) ~ 500m2/g, mean pore size 60Å, specific pore volume 0.75ml/g,
particle size 2 to 10 µm
outstanding hardness and abrasion resistance due to an optimized binder system increased separation efficiency due to an optimized particle size distribution high suitability for trace analyses resulting from a UV indicator with increased brilliance and a low-noise background of the layer narrow fractionation of the silica particles allows theoretical plate heights, which are one order of magnitude smaller than on standard silica layers with the advantage of sharper separations, shorter developing times, shorter migration distances, lower amount of samples, and increased detection sensitivity with equal selectivity.
Available as glass plates with or without fluorescent indicator (UV 254).
Toote variatsioonid
| Catalog number | PK | Dimensions (WxL) | Film thickness | Length | Material | Particle size | Type | Width | Kogus | |
|---|---|---|---|---|---|---|---|---|---|---|
| 6.226 346 | 25.00 | 100 x 100 mm | 200 µm | 100 mm | Glass | 2...10 µm | Nano-ADAMANT UV254 | 100 mm | ||
| 4.005 072 | 50.00 | 100 x 200 mm | 200 µm | 200 mm | Glass | 2...10 µm | Nano-ADAMANT UV254 | 100 mm | ||
| 4.005 075 | 50.00 | 100 x 200 mm | 200 µm | 200 mm | Glass | 2...10 µm | Nano-ADAMANT | 100 mm | ||
| 4.005 074 | 25.00 | 100 x 100 mm | 200 µm | 100 mm | Glass | 2...10 µm | Nano-ADAMANT | 100 mm |